Effect of nitridation temperature on TiO2 nanotubular structure and its photoelectrochemical performance T. Lemes , S. Khan, E. Leal da Silva, L. L. de Costa, S. R. Teixeira, C. Aguzzoli, C.F. Malfatti   2018/04/20

Abstract

To improve light absorption in the visible region and to improve photoelectrochemical (PEC) response; herein, we have presented the doping of titanium dioxide (TiO2) nanotubes with nitrogen. TiO2 nanotubes have been heat treated under the ammonia environment at different temperatures for 3 h. The characterization was carried out using field emission gun scanning electron microscopy, (FEG-SEM), visible ultraviolet (UV-Vis) spectrophotometry. The photoelectrochemical tests of the samples were carried out in a Na2S/Na2SO3 (aq) solution. It was found that the nitrogen doping of titanium dioxide in temperature above 600 °C collapses the tubular structure and decreases the PEC performance. On the other hand, PEC performance improving was obtained from the sample nitrided at the lower temperatura which is related to the formation of lower defects in the structure of TiO2 nanotubes.

Authors and affiliations

T. Lemes *, S. Khan2, E. Leal da Silva1,L. L. de Costa3, S. R. Teixeira2, C. Aguzzoli4, C.F. Malfatti1
1. LAPEC/PPGE3M, Universidade Federal do Rio Grande do Sul, Porto Alegre/RS (Brazil)
2. Instituto de Física, Universidade Federal do Rio Grande do Sul, Porto Alegre/RS (Brazil)
3. LDTM/PPGE3M, Universidade Federal do Rio Grande do Sul, Porto Alegre/RS (Brazil)
4. PGMAT/UCS, Universidade de Caxias do Sul, Caxias do Sul, RS, Brasil

Key words

Anodizing, Nanotubes, Titanium dioxide, Photoelectrocatalysis, Nitridation

References

[1] K. Nakata, A Fujishima, “TiO2 photocatalysis: design and applications.” J. Photochem. Photobiol. C photochem. Rev. (2012);13:169–189.
[2] A. Kudo, Y. Received. “Renewable energy issue energy research.” Chem. Soc. Rev. (2008); 38: 253–278.
[3] S. Khan, M. “Pristine Ta3N5 Nanotubes: Trap-Driven High External Biasing Perspective in Semiconductor/Electrolyte Interfaces”. Chermistry a European Journal. (2016); 22: 18501–18511.
[4] J. Fernandes, P. Migowski, Z. Fabrim et al. “Magnetron sputtering for photoelectrochemical applications under visible light irradiation.” Phys. Chem. (2014); 9148-9153.
[5] B. Yuana, Y. Wang. “Nitrogen doped TiO2 nanotube arrays with high photoelectrochemical activity for photocatalytic applications Applied Surface”. Science (2013); 280: 523– 529.
[6] L. Haijin, L. Guoguang. “Gd3+ N-codoped trititanate nanotubes: preparation, characterization and photocatalytic activity”. Applied Surface Science (2011); 257: 3728–3732.
[7] R. Yerga, M. Galván. “Water Splitting on Semiconductor Catalysts under Visible- Light Irradiation.” ChemSusChem (2009); 2: 471 – 485.
[8] T. dos Santos, K. Sherdil. “Efeito de potencial de anodização na propriedade fotoeletroquímica de nanotubos de TiO2.” 71º Congresso Anual da ABM (2006).
[9] S. Khan, M. Zapata. “Effect of oxygen content on the photoelectrochemical activity of crystallographically preferred oriented Porous Ta3N5 nanotubes”. J. Phys. Chem. C (2015); 119: 19906-19914.
[10] J. Fernandes, E. Kohlrausch “Effect of anodisation time and thermal treatment temperature on the structural and photoelectrochemical properties of TiO2 nanotubes”. Solid State Chemistry (2017); 251: 217-223.
[11] E. Kohlrausch, M. Zapata. “Polymorphic phase study on nitrogen-doped TiO2 nanoparticles: effect on oxygen site occupancy, dye sensitized solar cells efficiency and hydrogen production.” (2015); 123.
[12] S. Khan, M. Zapata. ”Structural, optical and photoelectrochemical characterizations of monoclinic Ta3N5 thin films.” Physical Chemistry (2015); 37: 23677-24480.